前处理对不同铝合金腐蚀性能及机制的影响

doi:10.3969/j.issn.2095-2198.2023.03.010

摘要
参考文献
相关文章
推荐阅读
Metrics

下载:

PDF (1674KB)
输出: BibTeX | EndNote (RIS)

摘要

为探究前处理对不同铝合金的腐蚀性能及腐蚀机制的影响，选取国产板材AA1060、AA2024、AA3003、AA5052和AA6061作为研究对象，通过中性盐雾试验和电化学测试对打磨处理前后的不同铝合金进行测试和表征.结果表明：打磨和未经打磨处理的铝合金经24 h中性盐雾试验后，表面出现不同程度的腐蚀；电化学测试结果表明，打磨前处理后，AA1060、AA2024、AA3003和AA5052铝合金的自腐蚀电位均有不同程度的降低，AA1060、AA3003和AA5052铝合金极化电阻均有不同程度的变大，对比发现，AA2024锈蚀最为严重.

	服务
	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	（）
	作者相关文章

关键词: 铝合金')" href="#">

铝合金防腐性能电化学

Abstract:

In order to explore the effect of pre-treatment on the corrosion performance and corrosion mechanism of different aluminum alloys,domestic sheets AA1060,AA2024,AA3003,AA5052,and AA6061 were selected as the research objects.Through neutral salt spray experiment and electrochemical test,different aluminum alloys before and after polishing treatment were tested and characterized.The results show that after 24 h of neutral salt spray test,the surface of the polished and unpolished aluminum alloys has different degrees of corrosion.The electrochemical test results show that the self-corrosion potential of AA1060,AA2024,AA3003,and AA5052 aluminum alloys decreases to varying degrees.And the polarization resistance of AA1060,AA3003,and AA5052 aluminum alloys al increases to varying degrees.The comparison shows that AA2024 is the most severely corroded.

Key words: aluminum alloy')" href="#">

aluminum alloy corrosion resistance electrochemistry

出版日期: 2023-06-30 发布日期: 2024-03-11 整期出版日期: 2023-06-30

ZTFLH:

TG172.2

作者简介: 李庆鹏(1984—)，男，辽宁沈阳人，讲师，博士，主要从事环保防护技术的研究.

引用本文:

李庆鹏1, 2, 刘利冉1, 李敏1, 史胜南2, 刘建国3.

前处理对不同铝合金腐蚀性能及机制的影响 [J]. 沈阳化工大学学报, 2023, 37(3): 266-271.
LI Qingpeng1, 2, LIU Liran1, LI Min1, SHI Shengnan2, LIU Jianguo3.

Effect of Pretreatment on Corrosion Performance and Mechanism of Different Aluminum Alloys . Journal of Shenyang University of Chemical Technology, 2023, 37(3): 266-271.

链接本文:

https://xuebao.syuct.edu.cn/CN/10.3969/j.issn.2095-2198.2023.03.010 或 https://xuebao.syuct.edu.cn/CN/Y2023/V37/I3/266

［1］崔继红,蔡建平,贾成厂.盐雾环境下高强度铝合金的点蚀行为［J］.中国腐蚀与防护学报,2010,30(3):107-202.

［2］PERKINS J,CUMMINGS J R,GRAHAM K J.Morphological Studies of Occluded Cells in the Pitting of Dilute Aluminum Alloys in Seawater［J］.Journal of the Electrochemical Society,2019,129(1):137-141.

［3］ MIRHASHEMIHAGHIGHI S,S′WIATOWSKA J,MAURICE V,et al.Corrosion Protection of Aluminium by Ultra-Thin Atomic Layer Deposited Alumina Coatings［J］.Corrosion Science,2016(106):16-24.

［4］杨卉芃,张亮,冯安生,等.全球铝土矿资源概况及供需分析［J］.矿产保护与利用,2016(6):64-70.

［5］杨欢,张弢，张志刚，等.铝合金支撑MFI型分子筛膜的合成及耐蚀性能研究［J］.沈阳化工大学学报,2013,27(3):202-208.

［6］KARKALOS N E，KARMIRIS-OBRATAN′SKI P，KURPIEL S，et al.Investigation on the Surface Quality Obtained during Trochoidal Milling of 6082 Aluminum Alloy［J］.Machines,2021,9(4):75.

［7］CAO H L，WANG J Q，TIAN Y X，et al.Prediction and Measurement of Quenching and Pre-Stretching Stress in 7050 Aluminum Alloy Thick Plate［J］.Materials Science Forum,2021,1026:109-114.

［8］NAEIMI M，EIVANI A R，JAFARIAN H R，et al.Correlation between Microstructure,Tensile Properties and Fatigue Life of AA1050 Aluminum Alloy Processed by Pure Shear Extrusion［J］.Materials Science and Engineering:A,2017,679:292-298.

［9］赵瓛，邓斌，周水清，等.3系铝合金微波组件壳体的激光封焊工艺研究［J］.电子工业专用设备,2019,48(4):47-51.

［10］ HOU J C，LI R F，XU C，et al.A Comparative Study on Microstructure and Properties of Pulsed Laser Welding and Continuous Laser Welding of Al-25Si-4Cu-Mg High Silicon Aluminum Alloy［J］.Journal of Manufacturing Processes,2021,68（Part A）:657-667.

［11］付广艳，钱神华，许文兰，等.Mg-xZn合金的制备及腐蚀性能研究［J］.沈阳化工大学学报,2020,34(3):250-254.

［12］邢俊红,赵强.铁硅比对连铸连轧8系铝合金组织及性能的影响［J］.中国金属通报,2019(10):110-111.

［13］马晋芳，杨玉芬.过时效热处理对LC9铝合金组织与性能的影响［J］.机械工程与自动化,2020(6):116-118.

［14］刘民章.1系变形铝合金熔铸工艺过程控制［J］.有色冶金节能,2021,37(1):17-22.［

［15］王海涛，任荣，冯业文，等.热挤压用2系铝合金铝棒毛坯的重力铸造工艺研究［J］.金属加工(热加工),2020(2):81-83.

［16］王雪莹，吴邵卿，王冰莹，等.3系铸造铝合金光谱与化学分析标准样品的研制［J］.化学分析计量,2017,26(6):4-10.

［17］HUANG L，CHEN X Z，KONOVALOV S，et al.The Effect of Wire Feeding Speed on Solidification Cracking of CMT Welding for Al-Si Alloys［J］.Metals,2021,11(2):267.

［18］苑锡妮，杨兵，曾渝.5×××系铝合金汽车板研究进展［J］.轻合金加工技术,2018,46(6):8-13，62.

［19］汪建强，郭丽丽.汽车用6×××系铝合金及其冲压成形性研究综述［J］.轻合金加工技术,2018,46(9):11-16.

［20］郑晓静.7系高强铝合金变形强化工艺与组织性能关系［J］.科技视界,2021,(4):56-58.

［21］付裕，马科，韩念梅，等.8×××铝合金箔表面白条缺陷的分析［J］.轻合金加工技术,2019,47(8):30-34.

［22］汪志佳，刘明玲.高压处理对LC9铝合金导电性能的影响［J］.热加工工艺,2014,43(2):50-51.

［23］PAN C G，GONG M C，FENG S Q，et al.Corrosion and Thermal Fatigue Behaviors of Induction-Clad Ni-Coated TiC Particle-Reinforced Ni60 Coating in Molten Aluminum Alloy［J］.Surface and Coatings Technology,2021,419:127278.

［24］鲁俊，梁英，汤尚文，等.无铬达克罗涂料工艺及耐蚀性能研究［J］.应用化工,2011,40(4):612-613,,617.

［25］张博，赵焕，董宇，等.2024铝合金表面有色钛锆转化膜的制备与性能研究［J］.材料保护， 2018,51(7):1-5,19.

［26］郭增昌,王云芳,王汝敏.铝合金表面不同硅烷化预处理的耐蚀性研究［J］.中国腐蚀与防护学报，2007,27(3):172-175,180.

［27］CAO C N.Journal of Chinese Society for Corrosion and Protection Introduction to Electrochemical Impedance Spectroscopy［M］.Beijing:Science Press,2002:26-27.

[1]	刘洋, 谭俊哲, 刘文英, 丛印齐, 赵亚楠. 高效无卤蚀刻体系对核级304不锈钢表面结构的影响 [J]. 沈阳化工大学学报, 2021, 35(4): 347-351.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed